Full metadata record
DC poleHodnotaJazyk
dc.contributor.authorKovářík, Tomáš
dc.contributor.authorKřenek, Tomáš
dc.contributor.authorRieger, David
dc.contributor.authorPola, Michal
dc.contributor.authorŘíha, Jan
dc.contributor.authorSvoboda, Miloš
dc.contributor.authorBeneš, Jan
dc.contributor.authorŠutta, Pavol
dc.contributor.authorBělský, Petr
dc.contributor.authorKadlec, Jaroslav
dc.date.accessioned2018-02-21T11:35:28Z-
dc.date.available2018-02-21T11:35:28Z-
dc.date.issued2017
dc.identifier.citationKOVÁŘÍK, T., KŘENEK, T., RIEGER, D., POLA, M., ŘÍHA, J., SVOBODA, M., BENEŠ, J., ŠUTTA, P., BĚLSKÝ, P., KADLEC, J. Synthesis of open-cell ceramic foam derived from geopolymer precursor via replica technique. Materials letters, 2017, roč. 209, č. 15 December 2017, s. 497-500. ISSN 0167-577X.en
dc.identifier.issn0167-577X
dc.identifier.urihttp://hdl.handle.net/11025/29299
dc.description.abstractTento článek popisuje snadnou a účinnou metodu pro výrobu keramické pěny s otevřenou pórovitostí na základě geopolymerního prekurzoru pomocí replikační metody. Metoda s využitím polyuretanové houby byla aplikována za použití geopolymerní směsi na bázi práškové směsi metakaolinu / vysrážené siliky, roztoku draselného a jemného šamotového plniva. Zrychlený krok vytvrzení při 60°C po dobu 30 minut byl proveden za účelem získání pevné struktury s dobrou přilnavostí k polymerní houbě. Byl zkoumán účinek tepelného zpracování na mechanické a strukturní chování syntetizovaných pěn. Analýza rentgenové difrakce (RTG) ukázala, že mezi tepelně exponovanými vzorky se neobjevily žádné podstatné rozdíly v obsahu krystalických fází Leucite – Křemičitan hlinito-draselný. Bylo zjištěno, že pevnost v tlaku keramických pěn dosáhla hodnoty 0,85 ± 0,11 MPa poté, co byly vzorky vystaveny výpalu při teplotě 1300°C. Navíc skenovací elektronová mikroskopie (SEM) a rentgenová mikro-tomografie (μ-CT) potvrdila uniformní vzájemně propojenou buněčnou strukturu s velikostí pórů mezi 1 až 2 mm a otevřenou pórovitostí (εo) 78,88% obj.cs
dc.format4 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherElsevieren
dc.rightsPlný text není přístupný.cs
dc.rights© Elsevieren
dc.subjectKeramické kompozitycs
dc.subjectPorézní materiálycs
dc.subjectPěna s otevřenou pórovitostícs
dc.subjectGeopolymercs
dc.subjectRentgenová mikro-tomografie (μ-CT)cs
dc.titleSyntéza keramické pěny s otevřenou pórovitostí připravenou z geopolymerního prekurzoru pomocí replikační metodycs
dc.titleSynthesis of open-cell ceramic foam derived from geopolymer precursor via replica techniqueen
dc.typečlánekcs
dc.typearticleen
dc.rights.accessclosedAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedThis paper describes a facile and effective method for fabrication of open-cell ceramic foam derived from geopolymer precursor through replica technique. The polyurethane sponge method was applied using geopolymer mixture based on powder mixture of metakaolin/precipitated silica, potassium silica solution and fine chamotte filler. Accelerated solidification step at 60 °C for 30 min was performed to obtain dense structure with a good adhesion to the polymeric sponge. The effect of thermal treatment on mechanical and structural behavior of synthesized foams was investigated. X-ray diffraction (XRD) analysis indicated that no substantial differences in the content of crystalline Leucite - Potassium Aluminum Silicate phases appeared between thermally treated samples at 1100 °C, 1200 °C and 1300 °C. It has been revealed that compression strength of ceramic foams reached 0.85 ± 0.11 MPa after the samples had been treated at 1300°C. In addition, scanning electron microscopy (SEM) and X-ray micro computed tomography (µ-CT) confirmed uniform interconnected cellular structure with pore sizes between 1 – 2 mm resulting in an open porosity (εo) of 78.88 vol%.en
dc.subject.translatedCeramic compositesen
dc.subject.translatedPorous materialsen
dc.subject.translatedOpen-cell foamen
dc.subject.translatedGeopolymeren
dc.subject.translatedX-ray micro computed tomography (μ-CT)en
dc.identifier.doi10.1016/j.matlet.2017.08.081
dc.type.statusPeer-revieweden
dc.identifier.obd43920825
dc.project.IDLO1402/CENTEM+cs
Vyskytuje se v kolekcích:Články / Articles (CTM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Kovarik_Synthesis of open-cell.pdf1,13 MBAdobe PDFZobrazit/otevřít  Vyžádat kopii


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/29299

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD