| Název: | Vysokoteplotní odolnost proti opotřebení a oxidaci HVOF povlaků na bázi CrC The High-Temperature Wear and Oxidation Behavior of CrC-Based HVOF Coatings |
| Autoři: | Houdková, Šárka Česánek, Zdeněk Smazalová, Eva Lukáč, František |
| Citace zdrojového dokumentu: | HOUDKOVÁ, Š., ČESÁNEK, Z., SMAZALOVÁ, E., LUKÁČ, F. The High-Temperature Wear and Oxidation Behavior of CrC-Based HVOF Coatings. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2018, roč. 27, č. 1-2, s. 179-195. ISSN 1059-9630. |
| Datum vydání: | 2018 |
| Nakladatel: | Springer |
| Typ dokumentu: | článek article |
| URI: | 2-s2.0-85029431754 http://hdl.handle.net/11025/29793 |
| ISSN: | 1059-9630 |
| Klíčová slova: | HVOF, žárový nástřik, karbid chromu, oxidace, vysoká teplota, pára, opotřebení, energetika |
| Klíčová slova v dalším jazyce: | HVOF, thermal spray, chromium carbide, oxidation, high temperature, wear, power industry |
| Abstrakt: | Byly hodnoceny tři komerčně dostupné materiály na bázi CrC s rozdílnou matricí(Cr3C2-25%NiCr; Cr3C2-25%CoNiCrAlY and Cr3C2-50%NiCrMoNb), deponované pomocí technologie HVOF. Byla sledována jejich odolnost proti působení vyské teploty v různých typech prostředí - v horkém vzduchu a horké tlakové páře. Ukázalo se, že povlak Cr3C2-50%NiCrMoNb je vhodnou náhradou povlaku Cr3C2-25%NiC, který v prostředí horké tlakové páry podléhá preferenční oxidaci karbidických částic. |
| Abstrakt v dalším jazyce: | Three commercially available chromium carbide-based powders with different kinds of matrix (Cr3C2-25%NiCr; Cr3C2-25%CoNiCrAlY and Cr3C2-50%NiCrMoNb) were deposited by an HVOF JP-5000 spraying gun, evaluated and compared. The influence of heat treatment on the microstructure and properties, as well as the oxidation resistance in a hot steam environment (p=24 MPa; T=609°C) were evaluated by SEM and XRD with respect to their potential application in the steam power industry. The sliding wear resistance measured at room and elevated (T=600°C) temperatures according to ASTM G-133. For all three kinds of chromium carbide-based coatings the precipitation of secondary carbides from the supersaturated matrix was observed during the heat treatment. For Cr3C2-25%NiCr coating annealed in hot steam environment as well as for Cr3C2-25%CoNiCrAlY coating in both environment, the inner carbide oxidation was recorded. The sliding wear resistance was found equal at room temperature, regardless of the matrix composition and content, while at elevated temperatures, the higher wear was measured, varying in dependence on the matrix composition and content. The chromium carbide-based coating with modified matrix composition Cr3C2-50%NiCrMoNb is suitable to replace the Cr3C2-25%NiCr coating in a hot steam environment to eliminate the risk of failure caused by inner carbide oxidation |
| Práva: | Plný text není přístupný. © Springer Verlag |
| Vyskytuje se v kolekcích: | Články / Articles (CTM) OBD |
Soubory připojené k záznamu:
| Soubor | Velikost | Formát | |
|---|---|---|---|
| The High-Temperature Wear and Oxidation Behaviour of CrC-Based HVOF Coatings.pdf | 4,04 MB | Adobe PDF | Zobrazit/otevřít Vyžádat kopii |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/29793Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.