| Název: | High-temperature corrosion behavior of selected thermally sprayed coatings in corrosive aggressive environment |
| Další názvy: | Vysokoteplotní korozní chování vybraných žárově stříkaných povlaků v korozně agressivním prostředí |
| Autoři: | Česánek, Zdeněk Houdková Šimůnková, Šárka Lukáč, František |
| Citace zdrojového dokumentu: | ČESÁNEK, Z., HOUDKOVÁ ŠIMŮNKOVÁ, Š., LUKÁČ, F. High-temperature corrosion behavior of selected thermally sprayed coatings in corrosive aggressive environment. Materials Research Express, 2019, roč. 6, č. 1. ISSN 2053-1591. |
| Datum vydání: | 2019 |
| Nakladatel: | IOP Publishing |
| Typ dokumentu: | článek article |
| URI: | 2-s2.0-85056095632 http://hdl.handle.net/11025/31147 |
| ISSN: | 2053-1591 |
| Klíčová slova: | tepelně rozstřikovaný povlak;odolnost proti korozi;roztavené soli;Cr3C2-25% NiCr;stellite 6;hastelloy C-276 |
| Klíčová slova v dalším jazyce: | thermally sprayed coating;corrosion resistance;molten salts;Cr3C2-25% NiCr;stellite 6;hastelloy C-276 |
| Abstrakt: | Cílem článku je zhodnotit a porovnat korozní odolnost povlaku Hastelloy C-276 s povlakem Stellite 6 a Cr3C2-NiCr, deponovaných technologií HP/HVOF. Koroze byla testována pomocí směsi agresivních solí 40%Na2SO4-60% V2O5, simulujících prostředí spalovacích kotlů. Bylo realizováno 50 cyklů při teplotě 750°C a následné schlazení na pokojovou teplotu po dobu 20 min.Zkorodované vzorky byly testovány pomocí elektronového mikroskopu, a EDS analýz. V porovnání s Cr3C2-NiCr, povlaky Hastelloy a Stellite poskytly lepší ochranu. Korozní mechanismus Hastelloy C-276 je založen na tvorbě ochranné oxidické vrstvy, která brání dalšímu prnikání korozního média. Povlak Stellite 6 korodoval pohranicích jednotlivých splatů, což vedlo k jejich postupnému odloupávání. V případě povlaku Cr3C2-NiCr byla korozně napadena matrice, což vedlo k postupnému uvolňování karbidů a destrukci povlaku. |
| Abstrakt v dalším jazyce: | The aim of this paper is to evaluate and compare the corrosion resistance of Hastelloy C-276 coating with Stellite 6 and Cr3C2%-25% NiCr coatings. The coatings were deposited usingHP/HVOF(High Pressure/High Velocity Oxygen Fuel) thermal spraying technology. The corrosion test was conducted in the corrosive-aggressive environment of molten salts mixture in the composition of 40% Na2SO4–60%V2O5, simulating the corrosion environment of boilers for residual fuel oils. The corrosion test under cyclic conditions included 50 cycles at the temperature of 750 °Cand subsequent cooling at the room temperature for 20 min. The corroded specimens were analyzed using scanning electron microscope (SEM) and elemental analysis (EDS). In comparison with Cr3C2-25% NiCr coating, both Stellite 6 and Hastelloy C-276 coatings provided the substrate material with sufficient protection against high-temperature corrosion. The corrosion mechanism of Hastelloy C-276 coating was based on the formation of protective oxide layer which prevented further penetration of corrosive media. Stellite 6 coating exhibited the corrosion attack along splat boundaries resulting in spat delaminating into the build-up. The corrosion mechanism of Cr3C2-25% NiCr coating included the attack on NiCr matrix resulting in gradual separation of carbide phases into the corrosive environment. |
| Práva: | Plný text není přístupný. © IOP Publishing |
| Vyskytuje se v kolekcích: | Články / Articles (KTO) OBD |
Soubory připojené k záznamu:
| Soubor | Velikost | Formát | |
|---|---|---|---|
| Česánek_2019_Mater._Res._Express_6_016426-1.pdf | 1,28 MB | Adobe PDF | Zobrazit/otevřít Vyžádat kopii |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/31147Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.