dc.identifier.citationČESÁNEK, Z., HOUDKOVÁ ŠIMŮNKOVÁ, Š., LUKÁČ, F. High-temperature corrosion behavior of selected thermally sprayed coatings in corrosive aggressive environment. Materials Research Express, 2019, roč. 6, č. 1. ISSN 2053-1591.en
dc.identifier.issn2053-1591
dc.identifier.uri2-s2.0-85056095632
dc.identifier.urihttp://hdl.handle.net/11025/31147
dc.description.abstractCílem článku je zhodnotit a porovnat korozní odolnost povlaku Hastelloy C-276 s povlakem Stellite 6 a Cr3C2-NiCr, deponovaných technologií HP/HVOF. Koroze byla testována pomocí směsi agresivních solí 40%Na2SO4-60% V2O5, simulujících prostředí spalovacích kotlů. Bylo realizováno 50 cyklů při teplotě 750°C a následné schlazení na pokojovou teplotu po dobu 20 min.Zkorodované vzorky byly testovány pomocí elektronového mikroskopu, a EDS analýz. V porovnání s Cr3C2-NiCr, povlaky Hastelloy a Stellite poskytly lepší ochranu. Korozní mechanismus Hastelloy C-276 je založen na tvorbě ochranné oxidické vrstvy, která brání dalšímu prnikání korozního média. Povlak Stellite 6 korodoval pohranicích jednotlivých splatů, což vedlo k jejich postupnému odloupávání. V případě povlaku Cr3C2-NiCr byla korozně napadena matrice, což vedlo k postupnému uvolňování karbidů a destrukci povlaku.cs
dc.format9 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherIOP Publishingen
dc.rightsPlný text není přístupný.cs
dc.rights© IOP Publishingen
dc.subjecttepelně rozstřikovaný povlakcs
dc.subjectodolnost proti korozics
dc.subjectroztavené solics
dc.subjectCr3C2-25% NiCrcs
dc.subjectstellite 6cs
dc.subjecthastelloy C-276cs
dc.titleHigh-temperature corrosion behavior of selected thermally sprayed coatings in corrosive aggressive environmenten
dc.title.alternativeVysokoteplotní korozní chování vybraných žárově stříkaných povlaků v korozně agressivním prostředícs
dc.typečlánekcs
dc.typearticleen
dc.rights.accessclosedAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedThe aim of this paper is to evaluate and compare the corrosion resistance of Hastelloy C-276 coating with Stellite 6 and Cr3C2%-25% NiCr coatings. The coatings were deposited usingHP/HVOF(High Pressure/High Velocity Oxygen Fuel) thermal spraying technology. The corrosion test was conducted in the corrosive-aggressive environment of molten salts mixture in the composition of 40% Na2SO4–60%V2O5, simulating the corrosion environment of boilers for residual fuel oils. The corrosion test under cyclic conditions included 50 cycles at the temperature of 750 °Cand subsequent cooling at the room temperature for 20 min. The corroded specimens were analyzed using scanning electron microscope (SEM) and elemental analysis (EDS). In comparison with Cr3C2-25% NiCr coating, both Stellite 6 and Hastelloy C-276 coatings provided the substrate material with sufficient protection against high-temperature corrosion. The corrosion mechanism of Hastelloy C-276 coating was based on the formation of protective oxide layer which prevented further penetration of corrosive media. Stellite 6 coating exhibited the corrosion attack along splat boundaries resulting in spat delaminating into the build-up. The corrosion mechanism of Cr3C2-25% NiCr coating included the attack on NiCr matrix resulting in gradual separation of carbide phases into the corrosive environment.en
dc.subject.translatedthermally sprayed coatingen
dc.subject.translatedcorrosion resistanceen
dc.subject.translatedmolten saltsen
dc.subject.translatedCr3C2-25% NiCren
dc.subject.translatedstellite 6en
dc.subject.translatedhastelloy C-276en
dc.identifier.doi10.1088/2053-1591/aae956
dc.type.statusPeer-revieweden
dc.identifier.document-number448882200003
dc.identifier.obd43924245
dc.project.IDLO1402/CENTEM+cs
Vyskytuje se v kolekcích:Články / Articles (KTO)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Česánek_2019_Mater._Res._Express_6_016426-1.pdf1,28 MBAdobe PDFZobrazit/otevřít  Vyžádat kopii
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/31147

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD