| Title: | Influence of Austenite Grain Size on Mechanical Properties after Quench and Partitioning Treatment of a 42SiCr Steel |
| Other Titles: | Vliv velikosti austenitické zrna na mechanické vlastnosti oceli 42SiCr zpracované kalením a přerozdělením |
| Authors: | Härtel, Sebastian Awiszus, Birgit Graf, Marcel Nitsche, Alexander Böhme, Marcus Wagner, Martin F. X. Jirková, Hana Mašek, Bohuslav |
| Citation: | HÄRTEL, S., AWISZUS, B., GRAF, M., NITSCHE, A., BÖHME, M., WAGNER, M. F. X., JIRKOVÁ, H., MAŠEK, B. Influence of Austenite Grain Size on Mechanical Properties after Quench and Partitioning Treatment of a 42SiCr Steel. Metals, 2019, roč. 9, č. 5, s. 1-11. ISSN 2075-4701. |
| Issue Date: | 2019 |
| Publisher: | MDPI |
| Document type: | článek article |
| URI: | 2-s2.0-85067594096 http://hdl.handle.net/11025/34930 |
| ISSN: | 2075-4701 |
| Keywords: | kalení a přerozdělení (Q-P proces);austenitické zrno;martenzitická struktura;mechanické chování;zkouška tlakem |
| Keywords in different language: | quench and partitioning (Q-P) process;austenite grain;martensitic microstructure;mechanical behavior;upsetting test |
| Abstract: | Tento článek zkoumá vliv velikosti původního austenitického zrna během procesu kalení a přerozdělení (Q-P) na finální mechanické vlastnosti Q-P oceli. Rozdíly v rozložení velikosti austenitické zrna mohou způsobit např. nerovnoměrnou rychlost ohřevu polotovarů před kovacím procesem. Za účelem kvantifikování tohoto vlivu bylo na válcových vzorkách z oceli 42SiCr provedeno definované tepelné zpracování na dilatometru. Rozdílná velikost austenitická zrna byla dosažena tepelným zpracováním, které předcházelo vlastnímu Q-P procesu. Výsledné mechanické vlastnosti byly popsány zkouškou tlakem a odpovídající mikrostruktura byla analyzována pomocí skenovacího elektronového mikroskopu (SEM). |
| Abstract in different language: | This paper examines how the initial austenite grain size in quench and partitioning (Q-P) processes influences the final mechanical properties of Q-P steels. Differences in austenite grain size distribution may result, for example, from uneven heating rates of semi-finished products prior to a forging process. In order to quantify this influence, a carefully defined heat treatment of a cylindrical specimen made of the Q-P-capable 42SiCr steel was performed in a dilatometer. Different austenite grain sizes were adjusted by a pre-treatment before the actual Q-P process. The resulting mechanical properties were determined using the upsetting test and the corresponding microstructures were analyzed by scanning electron microscopy (SEM). These investigations show that a larger austenite grain size prior to Q-P processing leads to a slightly lower strength as well as to a coarser martensitic microstructure in the Q-P-treated material. |
| Rights: | © MDPI © Creative Commons Attribution License 4.0 |
| Appears in Collections: | Články / Articles (RTI) OBD |
Files in This Item:
| File | Size | Format | |
|---|---|---|---|
| metals-09-00577.pdf | 21,08 MB | Adobe PDF | View/Open |
Please use this identifier to cite or link to this item:
http://hdl.handle.net/11025/34930Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.