| Název: | Influence of hardmetal feedstock powder on the sliding wear and impact resistance of High Velocity Air-Fuel (HVAF) sprayed coatings |
| Další názvy: | Vliv výchozího prášku na odolnost proti koluznému opotřebení a cyklickému impaktnímu namáhání HVAF nástřiku. |
| Autoři: | Lyphout, Christophe Bolelli, Giovanni Karhanová, Eva Sato, Kazuto Yamada, Junya Houdková Šimůnková, Šárka Lusvarghi, Luca Manfredini, Tiziano |
| Citace zdrojového dokumentu: | LYPHOUT, C. H., BOLELLI, G., KARHANOVÁ, E., SATO, K., YAMADA, J., HOUDKOVÁ ŠIMŮNKOVÁ, Š., LUSVARGHI, L., MANFREDINI, T. Influence of hardmetal feedstock powder on the sliding wear and impact resistance of High Velocity Air-Fuel (HVAF) sprayed coatings. WEAR, 2019, roč. 430, č. JUL 15 2019, s. 340-354. ISSN 0043-1648. |
| Datum vydání: | 2019 |
| Nakladatel: | Elsevier |
| Typ dokumentu: | článek article |
| URI: | 2-s2.0-85066275915 http://hdl.handle.net/11025/35986 |
| ISSN: | 0043-1648 |
| Klíčová slova: | Žárový nástřik;cermet;kluzné opotřebení;impaktní namáhání;metoda konečných orvků |
| Klíčová slova v dalším jazyce: | Thermal spray coatings;cermets;sliding wear;impact wear;finite element modelling |
| Abstrakt: | Práce je objasňuje, jak charakter WC-CoCr prášku, zejména velikost WC a matrice a pevnost jejich vzájemné vazby ovlivňuje kluzné třecí vlastnosti a odolnost proti cyklickému impaktnímu zatěžování povlaků deponovaných pomocí HVAF technologie. |
| Abstrakt v dalším jazyce: | The present work aimed to clarify how the characteristics of WC-CoCr hardmetal feedstock powders, namely thegrain size of the WC carbides and of the binder and the compressive strength of the sintered aggregates, affect the dry sliding wear and impact resistance of coatings deposited by High Velocity Air-Fuel (HVAF) spraying. Ball-on-Disc tests, which mimic a sliding wear process in the presence of hard asperities as it may occur e.g. in hydraulic seal joints or papermaking components, resulted in mild wear through near-surface microscale plasticflow, the exact nature of which was significantly affected by WC size. Finite element simulations of a singleasperity sliding process indeed showed that large WC grains concentrate contact stresses, thus undergoing very localised deformation. It is experimentally seen that repeated deformation of the carbide grains resulted in their cracking and pull-out. Uniformly distributed, fine carbides allowed the matrix to take on some stress, thus undergoing more homogeneous plastic flow. Block-on-Ring tests elicited adhesive wear as it may happen e.g. in metal-to-metal contacts (e.g. petrochemical valves). This could be effectively restrained by low matrix mean free path. Cyclic impact resistance of coarse-grained coatings was better than that of fine-grained ones, because of better large-scale cohesive strength. |
| Práva: | Plný text není přístupný. © Elsevier |
| Vyskytuje se v kolekcích: | Články / Articles (CT3) OBD |
Soubory připojené k záznamu:
| Soubor | Velikost | Formát | |
|---|---|---|---|
| Houdko_Influence of hardmetal feedstock powder on the sliding wear and impact.pdf | 11,04 MB | Adobe PDF | Zobrazit/otevřít Vyžádat kopii |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/35986Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.