Title: Degradation of Sintered Carbides in Different Corrosive Environments
Other Titles: Degradace slinutých karbidů v různých korozních prostředích
Authors: Bricín, David
Pomahač, Jiří
Kříž, Antonín
Citation: BRICÍN, D., POMAHAČ, J., KŘÍŽ, A. Degradation of Sintered Carbides in Different Corrosive Environments. In: Proceedings of the 30th International DAAAM Symposium "Intelligent Manufacturing & Automation". Vídeň: DAAAM International Vienna, 2019. s. 0646-0653. ISBN 978-3-902734-22-8 , ISSN 1726-9679.
Issue Date: 2019
Publisher: DAAAM International Vienna
Document type: konferenční příspěvek
conferenceObject
URI: 2-s2.0-85077912244
http://hdl.handle.net/11025/36638
ISBN: 978-3-902734-22-8
ISSN: 1726-9679
Keywords: Slinuté karbidy;korozní odolnost;degradační rychlost;WC-Co;WC-Ni
Keywords in different language: Sintered Carbide;corrosion resistance;the rate of degradation;WC-Co;WC-Ni
Abstract: Cílem studie bylo zjistit odolnost různých typů slinutých karbidů proti korozi v alkalickém a kyselém prostředí. Degradační prostředí pro slinuté karbidy byla vybrána tak, aby jejich pH odpovídala těm, s nimiž tyto karbidy normálně přicházejí do styku během jejich použití jako obráběcí nástroje nebo vrtací nástroje používané v těžebním průmyslu. Jako experimentální materiály byly vybrány slinuté karbidy na bázi WC-Co a WC-Ni. Zvolené materiály se lišily obsahem pojiva a velikostí zrn WC. Jako degradační médium byly vybrány tři alkalická média a tři kyselá média s hodnotami pH 0, 2, 7 a 12. Při experimentu byla pozorována rychlost, rozpuštění slinutého karbidu. Kromě stanovení míry rozpustnosti pojiva byla hodnocena korozní odolnost slinutých karbidů pomocí potenciostatu a frakce pojiva v rozpouštědlech pomocí atomové absorpční spektrometrie. Experimenty například ukázaly, že nejvyšší množství pojiva Co, bylo rozpuštěno v roztocích s vysokým obsahem kyseliny sírové. Na rozdíl od roztoku NaOH nebo CH3COOH.
Abstract in different language: The aim of the study was to determine the corrosion resistance of different types of sintered carbides in alkaline and acidic environments. The degradation environment for sintered carbides was chosen so that its pH corresponds to those with which these carbides normally come into contact during their use as machining tools or drilling tools used in the extractive industry. The experimental material was selected from sintered carbides based on WC-Co and WC-Ni. The materials chosen differed in the contents of the binder and the grain size of the WC. Three alkaline media and three acidic media were selected as the degradation media, with pH values of 0, 2, 7 and 12, in which the rate at which dissolution of the cemented carbide was observed. In addition to determining the solubility rate of the binder, the corrosion resistance of sintered carbides was evaluated using a potentiostat and the binder fraction in the solvents using atomic absorption spectrometry. The experiments showed, for example, that the highest amount of binder in sintered carbides with a cobalt binder was dissolved in solutions with high sulphuric acid content. In contrast with the solution of NaOH or CH3COOH.
Rights: © DAAAM International Vienna
Appears in Collections:Konferenční příspěvky / Conference papers (KMM)
OBD

Files in This Item:
File SizeFormat 
Bricin_DAAAM_2019.pdf1,07 MBAdobe PDFView/Open


Please use this identifier to cite or link to this item: http://hdl.handle.net/11025/36638

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

search
navigation
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD