Full metadata record
DC poleHodnotaJazyk
dc.contributor.authorBricín, David
dc.contributor.authorŠpirit, Zbyněk
dc.contributor.authorKříž, Antonín
dc.date.accessioned2021-03-01T11:00:27Z-
dc.date.available2021-03-01T11:00:27Z-
dc.date.issued2020
dc.identifier.citationBRICÍN, D., ŠPIRIT, Z., KŘÍŽ, A. Influence of boridation on microstructure and properties of aluminium alloy EN AW-2024. In: 31th DAAAM International Symposium on Intelligent Manufacturing and Automation. Viena: DAAAM International, 2020. s. 0477-0484. ISBN 978-3-902734-29-7, ISSN 1726-9679.cs
dc.identifier.isbn978-3-902734-29-7
dc.identifier.issn1726-9679
dc.identifier.uri2-s2.0-85098115038
dc.identifier.urihttp://hdl.handle.net/11025/42784
dc.description.abstractCílem této případové studie bylo provést analýzu vlivu procesu boridování na strukturu a mechanické vlastnosti hliníkové slitiny ENAW-2024. Připravené vzorky byly zpracovány za různých procesních parametrů v zásypu prášku Durferit. Po provedení chemicko-tepelného zpracování, byly hodnoceny změny v mikrostruktuře vzorků s použitím metod světelné a skenovací elektronové mikroskopie. Fázové složení vzorků bylo stanoveno s použitím RTG difrakční analýzy. Změny v mechanických vlastnostech byly posouzeny na základě provedené analýzy tvrdosti povrchové vrstvy a substrátu vzorků, zkouškou tvrdosti podle Vickerse. U vzorků byl dále změřen korozní odpor vůči zvolenému koroznímu prostředí 5% roztoku NaCl pomocí potenciostatu a odolnost vůči tribologickému otěru metodou Ball on disk. Na základě získaných dat je například možné uvést, že při procesu boridování této slitiny je důležité zamezit vzniku pasivační vrstvy Al2O3 před a v průběhu procesu chemicko-tepelného zpracování. Toho je možné docílit například okamžitým nanesením boridovacího přípravku případně jiného prostředku, který zamezí interakci kyslíku s povrchem upravovaného vzorku. U vzorků po procesu boridování byl dále zaznamenán nárůst odporu vůči použitému koroznímu prostředí 5% roztoku NaCl a Nižší hodnota koeficientu opotřebení oproti vzorkům bez provedeného chemicko-tepelného zpracování.cs
dc.format8 s.cs
dc.format.mimetypeapplication/pdf
dc.language.isoenen
dc.publisherDAAAM Internationalen
dc.relation.ispartofseries31th DAAAM International Symposium on Intelligent Manufacturing and Automationen
dc.rights© DAAAM Internationalen
dc.subjectboridovánícs
dc.subjectEN AW 2024cs
dc.subjectodolnost proti opotřebenícs
dc.subjectprecipitátycs
dc.subjectkorozní odolnostcs
dc.titleInfluence of boridation on microstructure and properties of aluminium alloy EN AW-2024en
dc.title.alternativeVliv boridování na mikrostrukturu a vlastnosti hliníkové slitiny EN AW-2024cs
dc.typekonferenční příspěvekcs
dc.typeconferenceObjecten
dc.rights.accessopenAccessen
dc.type.versionpublishedVersionen
dc.description.abstract-translatedThe aim of this case study was to analyse the influence of the boriding process on the structure and mechanical properties of the aluminium alloy EN AW 2024. The prepared samples were processed under various process parameters in Durferrit powder. After chemical-thermal treatment, changes in the microstructure of the samples were evaluated using light and scanning electron microscopy methods. Changes in mechanical properties were assessed on the basis of the analysis of the hardness of the sample substrate using the Vickers hardness test. The samples were further measured for corrosion resistance to the selected corrosion environment of 5% NaCl solution using a potentiostat and resistance to tribological abrasion by the Ball on-disk method. Based on the obtained data, it can be stated, for example, that during the boriding process of this alloy it is important to prevent the formation of a passivation layer of Al2O3 before and during the process of chemical-thermal treatment. This can be achieved, for example, by immediate application of a boriding agent or other agent which prevents the interaction of oxygen with the surface of the sample to be treated. The samples after the boriding process also showed an increase in the resistance to the used corrosive environment of 5% NaCl solution and a lower value of the wear coefficient compared to the samples without chemical-thermal treatment.en
dc.subject.translatedboridingen
dc.subject.translatedEN AW 2024en
dc.subject.translatedwear resistanceen
dc.subject.translatedprecipitatesen
dc.subject.translatedcorrosion resistanceen
dc.identifier.doi10.2507/31st.daaam.proceedings.067
dc.type.statusPeer-revieweden
dc.identifier.obd43931888
dc.project.IDSGS-2018-051/Aplikace nových postupů úpravy a testování povrchu i objemových materiálů za účelem zvýšení uplatnitelnosti konstrukčního celku nebo pracovního nástroje v průmyslové praxics
Vyskytuje se v kolekcích:Konferenční příspěvky / Conference papers (KMM)
OBD

Soubory připojené k záznamu:
Soubor VelikostFormát 
Bricin_01_DAAAM_2020.pdf1,23 MBAdobe PDFZobrazit/otevřít
Zobrazit minimální záznam Zobrazit statistiky


Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam: http://hdl.handle.net/11025/42784

Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.

hledání
navigace
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD