Title: Changes in Structure and Corrosion Resistance of Cryogenically Treated WC-Co Cemented Carbides
Other Titles: Změny ve struktře a korozní odolnosti kryogenně zpracovaných slinutých karbidů WC-Co
Authors: Bricín, David
Průcha, Vojtěch
Jansa, Zdeněk
Kříž, Antonín
Citation: BRICÍN, D. PRŮCHA, V. JANSA, Z. KŘÍŽ, A. Changes in Structure and Corrosion Resistance of Cryogenically Treated WC-Co Cemented Carbides. In 9th Manufacturing Engineering Society International Conference (MESIC 2021). Bristol: IOP Publishing LTD, 2021. s. nestránkováno. ISBN: neuvedeno , ISSN: 1757-8981
Issue Date: 2021
Publisher: IOP Publishing LTD
Document type: konferenční příspěvek
ConferenceObject
URI: http://hdl.handle.net/11025/51713
ISSN: 1757-8981
Keywords: WC-Co;slinuté karbidy;hluboké kryogenní zpracování (DCT);korozní odolnost;transformace kobaltu
Keywords in different language: WC-Co;cemented carbides;deep cryogenic treatment (DCT);corrosion resistance;transformation of cobalt
Abstract: Článek se zabývá hlubokým kryogenním zpracováním (DCT) slinutých karbidů (SK) typu WC-Co. K experimentu byly vybrány čtyři sort SK, které se lišily hrubostí zrn WC a objemem pojiva Co. U části vzorků bylo provedeno jejich DCT zpracování při teplotě -186 0C v prostředí kapalného dusíku. Druhá část vzorků byla popuštěna při teplotě 450 0C. U zpracovaných vzorků byla následně provedena analýza změn v jejich korozní odolnosti v prostředí uměle připravené důlní vody potenciodynamickou zkouškou. Změny v mikrostruktuře analyzovaných vzorků byly hodnoceny s použitím RTG difrakční anlýzy. Výsledky experiment ukázaly, že vzorky po DCT procesu mají vyšší korozní odolnost vůči vzorkům bez tohoto zpracování a vzorkům popuštěným. RTG difrakční analýza prokázala, že při DCT zpracování vzorků došlo ke změně podílu fází ε-Co a α-Co. Podíl takto přeměněné faze závisel na hrubosti zrn karbidické faze a podílu pojiva Co.
Abstract in different language: Deep cryogenic treatment (DCT) of WC-Co cemented carbides (CC) was experimentally explored. Four types of cemented carbides were studied. They had different WC grain sizes and the volume fractions of the cobalt binder. Some specimens were deep-cryogenic-treated (DCT) at -186°C in dry vapour of liquid nitrogen. Another group of specimens was tempered at 450°C. The corrosion resistance of treated specimens was then determined by potentiodynamic testing in artificial mine water. Microstructural changes were characterized with the aid of X-ray diffraction analysis. DCT-treated specimens showed a higher corrosion resistance than the untreated ones and than those which were only tempered. X-ray diffraction analysis revealed that DCT changed the ratio of ε-Co and α-Co phases. The extent of these transformations was dictated by the carbide phase grain size and by the volume fraction of cobalt.
Rights: © Creative Commons Attribution 3.0 licence
Appears in Collections:Konferenční příspěvky / Conference papers (RAM)
Konferenční příspěvky / Conference papers (KMM)
OBD

Files in This Item:
File SizeFormat 
Bricín_2021_IOP_Conf._Ser.__Mater._Sci._Eng._1193_012013.pdf677,59 kBAdobe PDFView/Open


Please use this identifier to cite or link to this item: http://hdl.handle.net/11025/51713

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

search
navigation
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD