Název: | Effect of processing parameters on microstructure and properties of CuSn10P1 alloy fabricated by SLM |
Autoři: | Polak, Marcin Radon, Adrian Hawelek, Lukasz Wlodarczyk, Patryk Kaminska, Malgorzata Osadnik, Malgorzata Juszczyk, Barbara Burian, Wojciech Kolano-Burian, Aleksandra |
Citace zdrojového dokumentu: | JIRKOVÁ, Hana ed.; JENÍČEK, Štepán ed. Proceedings PING 2019: modern trends in material engineering: 10.-13.09.2019, Pilsen. 1. vyd. Plzeň: University of West Bohemia, 2019, s. 14. ISBN 978-80-261-0879-5. |
Datum vydání: | 2019 |
Nakladatel: | University of West Bohemia |
Typ dokumentu: | konferenční příspěvek conferenceObject |
URI: | http://hdl.handle.net/11025/35208 |
ISBN: | 978-80-261-0879-5 |
Klíčová slova: | výroba aditiv;3D tisk;slitiny mědi a cínu;selektivní laserové tavení |
Klíčová slova v dalším jazyce: | additive manufacturing;3D printing;Cu-Sn alloys;selective laser melting |
Abstrakt v dalším jazyce: | The interest in Cu-Sn alloys is associated with excellent flexibility, wear and corrosion resistance, and high mechanical strength. CuSn10P1 alloy has the widest applications among Cu-Sn alloys and is widely used in the shaft sleeve, bearing, gears, valves, etc. The properties of this alloy are strongly depended to the manufacturing process. Usage of the traditional casting causes the intergranular segregation and crystallization of primary α-Cu phase in a coarse mesh dendritic structure. This, in turn, manifest itself in poor properties, limiting its uses in industry. According to that new manufacturing methods should be used to improve the properties of this alloy. In this work, CuSn10P1 alloy was successfully produced using selective laser melting (SLM). The powder size was between 20-63 µm and its humidity during the process was lower than 5%. The four printing strategies were selected to investigate the impact of printing parameters on the microstructure and mechanical properties of the prints. The optimal processing conditions were chosen on the basis of optimization of laser power and scanning speed. The different process parameters result in the changes of the microstructure, especially porosity and the presence of microcracks. On the basis of the analysis of wavelength-dispersive X-ray spectroscopy, it was confirmed, that all chemical elements are evenly distributed after selective laser melting. The segregation of tin and copper can be also observed, however only under remelting of the same layer. |
Práva: | © University of West Bohemia |
Vyskytuje se v kolekcích: | Proceedings PING 2019: modern trends in material engineering Proceedings PING 2019: modern trends in material engineering |
Soubory připojené k záznamu:
Soubor | Popis | Velikost | Formát | |
---|---|---|---|---|
Polak.pdf | Plný text | 180,85 kB | Adobe PDF | Zobrazit/otevřít |
Použijte tento identifikátor k citaci nebo jako odkaz na tento záznam:
http://hdl.handle.net/11025/35208
Všechny záznamy v DSpace jsou chráněny autorskými právy, všechna práva vyhrazena.