Title: Chemical heterogeneity of Inconel 625 overlay with an increased molybdenum content and its evaluation using the potentiodynamic corrosion test
Other Titles: Chemická heterogenita laserem navařené slitiny Inconel 625 se zvýšeným obsahem molybdenu hodnocená pomocí potenciodynamické korozní zkoušky
Authors: Bartoň Klufová, Pavla
Vostřák, Marek
Kříž, Antonín
Citation: BARTOŇ KLUFOVÁ, P., VOSTŘÁK, M., KŘÍŽ, A. Chemical heterogeneity of Inconel 625 overlay with an increased molybdenum content and its evaluation using the potentiodynamic corrosion test. In: Conference Proceedings - METAL 2019 - 28th International Conference on Metallurgy and Materials. Ostrava: Tanger, 2019. s. 962-967. ISBN 978-80-87294-92-5.
Issue Date: 2019
Publisher: Tanger
Document type: konferenční příspěvek
conferenceObject
URI: 2-s2.0-85079407947
http://hdl.handle.net/11025/42743
ISBN: 978-80-87294-92-5
Keywords: Laserové navařování;Inconel 625;heterogenita;potenciodynamická korozní zkouška
Keywords in different language: Laser cladding;Inconel 625;heterogeneity;potentiodynamic corrosion test
Abstract: Příspěvek je zaměřen na detailní analýzu chemické heterogenity laserových návarů Inconel 625 se zvýšeným obsahem molybdenu. V rámci experimentálního programu bylo připraveno celkem 5 kusů vzorků laserových návarů o celkové ploše 100*150 mm/návar. Jako substrát byla použita ocel S355J2 o tloušťce 50 mm. Během procesu navařování bylo u vybraných vzorků monitorováno rozložení teplotního pole na čelní ploše substrátu z oceli S355J2 pomocí termovizní kamery. Po obrobení povrchu laserového návaru na jeho užitnou výšku byly pomocí potenciodynamické korozní zkoušky stanoveny ustálený korozní potenciál, polarizační odpor a korozní rychlost ve vybraných oblastech laserového návaru. Dosažené výsledky byly hodnoceny s ohledy na ohřev substrátu během laserového navařování a metalografickou strukturu laserového návaru Inconel 625 se zvýšeným obsahem molybdenu.
Abstract in different language: The paper focuses on a detailed analysis of chemical heterogeneity of Inconel 625 overlays with an increased molybdenum content deposited by laser cladding. Fifteen samples of laser overlays on S355J2 steel were prepared, each with an area of 90×140 mm. The thickness of the steel substrate was 50 mm. During the laser cladding process, the temperature field on the face of the substrate was monitored by means of a thermal imaging camera. The surfaces of the Inconel 625 overlays were then machined to their final thickness. Corrosion potential, polarization resistance and corrosion rate in selected areas of laser clads were determined by the potentiodynamic corrosion test. These data were correlated with the temperature profiles during laser cladding and with microstructures of the overlays.
Rights: Plný text je přístupný v rámci univerzity přihlášeným uživatelům.
© Tanger
Appears in Collections:Konferenční příspěvky / Conference papers (CT3)
Konferenční příspěvky / Conference Papers (CTM)
Konferenční příspěvky / Conference papers (KMM)
OBD

Files in This Item:
File SizeFormat 
metal2019_klufova_metal_clanek1.pdf473,76 kBAdobe PDFView/Open    Request a copy


Please use this identifier to cite or link to this item: http://hdl.handle.net/11025/42743

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

search
navigation
  1. DSpace at University of West Bohemia
  2. Publikační činnost / Publications
  3. OBD